BD116 high temperature abrasion wearing resistant iron repair putty epoxy compound used in repairing and protecting the gray iron,ductile iron,cast iron parts defect and iron parts wear under the high temperature working condition:
Product description of BD116 metal iron wear abrasion high temperature resistant epoxy repair putty compound:
It’s the high temperature high performance polymerization metal materials compounded by various alloy material
and modified toughening heat resistant resin.The highest temperature resistance is 300 degree,suitable for the
repairing of gray iron,ductile iron,cast iron parts defect and iron parts wear under the high temperature
working condition.The color after repairing is basically the same as the substrates,with the very high strength and
excellent wear&corrosion resistance and aging resistant properties,can do various mechanical processing
together with substrates.
How to use of BD116 high temperature wearing resistant iron metal epoxy compound repair putty:
1.Surface treatment: Do the coarsening treatment on the pending-repair or needing-bonding area,
then clean it by cleaning agent.
2.Configuration: According to the mass ratio A:B=4:1 or volume ratio A:B=4:1,make A and B two components mix uniformly,
then use it up within specified operation time limit.
3.Coating: Make the mixed-up material spread coating on the pending-repair areas layer by layer,the first layer should be compacted,
make it infiltrate fully with the substrates.If the following working procedure needs machining,should keep out appropriate machining allowance
4.Curing: Curing for 2 hours at the temperature of 25-30 degree,heat it up to the temperature of 80 degree and keep this temperature
for 2 hours or it can be put into using after curing for 24 hours at the temperature of 25～30 degree,if the temperature is low,
should heat it up or prolong the curing time to promote the curing.
Performance index:
| product name | physical state | standard packaging | volume (cm3) |
operational time limit (25℃) |
usable time (25℃) |
| BD116 high temperature metal iron repair agent rebuilding epoxy compound |
paste | 250g/set Two-component |
178 | 45min | 24h |
| color | density (g/cm3) |
compressive strength (kg/cm2) GB1041-2008 |
shear strength (kg/cm2) GB7124-2008 |
bending strength (kg/cm2) GB1042-1999 |
hardness （Shore D） ASTM-D-2556 |
working temperature （℃） |
| iron cast | 1.41 | 971 | 149 | 482 | 86 | -60～250 |
Product packaging photo of our BD116 metal iron high temperature repair putty compound epoxy coating