cone crusher anti wear abrasion repair filled resin backing epoxy compound

Winter use notice of BD65 anti chemical impact corrosion abrasion wear resistant backing compound epoxy adhesive used in the cone crusher ceramic rubber lining plate repairing and protecting:

1.Cleaning up and preparation:
Clean up the residual filling material of the cone surface,or greasy dirt and dirt from the parts where touch with adhesive,
Fit up the cone and lining plate,seal up the cone/liner plate fitting surface and ring hole with adhesive tape etc,to avoid leaking
adhesive,in necessity,protect the screw thread on the axis,when using in winter,you had better heat up the A component to the
temperature of 30-40 degree separately to reduce viscosity for easy to pour before using.For ease of disassembly next time,
the cone and lining plate surface can precoat proper engine oil or mold release agent.

2.Configure adhesive:
Open the A component of BD65 crusher anti abrasion wear corrosion resistant repair epoxy adhesive backing compound,
stir it for 2 minutes with the electric blender,then make the B component pour into the A component drum at the same time stir
it with the electric blender,general stirring time is not more than 4 minutes,can make it mix uniformly.
Operation time:The total time from start mixing to finish filling is not more than 15 minutes(the data for 25 degree temperature)

Make the mixed-up BD65 crusher rubber lining pipeline repair epoxy compound backing adhesive solution pour into it along the cone
or a place of lining plate crack,easy to exhaust,in necessity,can make a cofferdam guide with plasticine etc,until overflow from the top
of crack.Don’t pour into the adhesive without mixing uniformly(with different colors).Perfusion therolling mortar wall,
before broken wall,remember to smear a layer of lubricating oil on the surface of adjusting sleeve body touching with filling material,
for easy to change the lining plate.

Place to cure for 12-24 hours at room temperature,the equipment can start up for running,when the temperature is too low in winter
(below 5 degree temperature),should heat up the pouring material to the temperature of 60-80 degree slowly after pouring,and keep
this temperature for 2 hours,after cooling it down slowly,it can be put into using.

Product usage of our BD65 crusher abrasion corrosion resistant repair backing epoxy compound:
BD65 crusher backing filling adhesive epoxy compound(crusher lining plate filling repair epoxy adhesive) is used in the
filling/supporting between crusher lining plate and substrates,gravel barrels and jacket gap,support cone and protective layer space,
at the same time it can be used as buffer material,when the equipment suffers impacting or load vibration from broken ore,
also used in the structural reinforcement,impact resistant vibration of ball mill wear resistant lining plate and cylinder gap.

Product packaging and actual picture shows:

Leave a Reply

Fill in your details below or click an icon to log in: Logo

You are commenting using your account. Log Out /  Change )

Google photo

You are commenting using your Google account. Log Out /  Change )

Twitter picture

You are commenting using your Twitter account. Log Out /  Change )

Facebook photo

You are commenting using your Facebook account. Log Out /  Change )

Connecting to %s