big particle ceramic bead filled epoxy repair compound wear resistant coating

The description of BD706 abrasion resistant large particle ceramic bead filled two component epoxy coatings:
http://www.wearcoating.com/case-of-desulfuration-pipeline-repairing-coatings/big_particle_ceramic_bead_filled_anti_wear_epoxy_coatings_4297.html

Packing specification of our BD706 large particles ceramic filled epoxy wear resistant coating:
Two component,10Kg/group,packed in a plastic drum
performance feature:
Wear resistant performance can reach even more than similar international  brand name products.
dark gray paste,large particle,room temperature curing
Excellent in wear & corrosion resistance
BD706 Abrasion Resistant coatings and the metal substrate with high bonding strength
Convenient for construction,without very high technical requirements for constructors
Suitable for the repairing and protecting of various wear,corrosion working condition
product usage:
It is the high performance wear & corrosion resistant polymerization ceramic material compounded by high performance wear
resistant ceramic particles and modified toughening resin.Widely used in the repairing of various wear-out parts and the preparation
of wear & corrosion resistant coating on the surface of various machine part which has wear resistant,corrosion resistant requirements,
such as the repairing and pre-protecting of large load fine particle erosive wear pump body,impeller,fan shell,pipeline elbow,
pipeline spiral conveyor etc.
How to use:
1.Surface treatment: Do coarsening treatment on the pending-repair part,grinding with angle grinder or sand blasting etc,
the surface after coarsening treatment should be cleaned,the surface after this treatment should be the one coarsening,
dry and fresh substrates,should be no greasy dirt and dust.
2.Preparation: According to weight ratio 4:1,make A and B two components mix uniformly,and use it up within 30 min.
Generally it’s while construction and configuration.Every time the most configuration quantity is not more than 1.5Kg,
too much adhesive is solidified too fast,hasn’t been used up until the adhesive has partial solidified and can’t be used.
According to the actual temperature,configuration can be properly a little more in winter and proper less in summer.
If the temperature is too low,can properly heat up the A component to reduce viscosity for easy to configure.
3.Coating: The suitable coating thickness of BD706 Abrasion Resistant coatings is 4~8mm,make the mixed-up material be
coating on the pending-repair part layer by layer,the first layer should be compacted,make it infiltrate fully with the substrates.
Repair the surface to be smooth after the coating is coated in the suitable size,or make BD426 be coating on the coating surface.
This material can’t do machining,should pay attention to controlling the coating thickness during repairing,in order to avoid
appearing interference phenomenon in the assembly.
4.Curing: Cure for 24 hours at the temperature of 25 degree before using,(If can heat up to the temperature of 60-80 degree
and keep this temperature for 2 hours,in this way,can improve 30% comprehensive performance) If the temperature is low,
should heat it up or prolong curing time to promote the curing.General construction in winter,can use iodine tungsten lamp
to do irradiation heating with 40cm distance from the coating.
706-%e4%b8%ad%e5%89%af%e6%9c%ac
Advertisements

Leave a Reply

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out / Change )

Twitter picture

You are commenting using your Twitter account. Log Out / Change )

Facebook photo

You are commenting using your Facebook account. Log Out / Change )

Google+ photo

You are commenting using your Google+ account. Log Out / Change )

Connecting to %s