high temperature metal repair epoxy wearing compound ceramic coating

BD115 high temperature resistant metal repair epoxy coating wearing compound
used in repairing and rebuilding various metal casting defects and parts wear abrasion,corrosion and fracture


Product description:
It’s the high temperature metal repairing agent consist of modified high temperature resin and high temperature curing agent,
made from filling-polymerization of ceramic,metal and so on.The highest temperature resistance is 300 degree,popular type,

Product usage of our BD115 metal high temperature resistant repair wearing compound epoxy coating:
Suitable for the repairing of various metal casting defects and parts abrasion wear,corrosion,fracture,with the higher strength and
excellent wear abrasion resistance,corrosion resistance and aging resistant properties after repairing,,can do various mechanical processing
together with substrates.

How to use:
1.Surface treatment: Do the coarsening treatment on the pending-repair or needing-bonding area,then clean it by cleaning agent.

2.Configuration: According to the mass ratio A:B=4:1 or volume ratio A:B=4:1, make A and B two components mix uniformly,then use it up
within specified operation time limit.

3.Coating: Make the mixed-up material spread coating on the pending-repair areas layer by layer,the first layer should be compacted,
make it infiltrate fully with the substrates.If the following working procedure needs machining,should keep out appropriate machining allowance.

4.Curing: cure for 2 hours at the temperature of 25~30 degree,heat it up to the temperature of 80 degree and keep this temperature for 2 hours
or cure for 24 hours at the temperature of 25~30 degree before using,if the temperature is low,should heat it up or prolong the curing time to
promote the curing.

Construction case photos of BD115 high temperature abrasion resistant metal repair compound epoxy coatings:



Leave a Reply

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out /  Change )

Google+ photo

You are commenting using your Google+ account. Log Out /  Change )

Twitter picture

You are commenting using your Twitter account. Log Out /  Change )

Facebook photo

You are commenting using your Facebook account. Log Out /  Change )


Connecting to %s