slurry recycle pipe rubber lining anti wearing repair compound epoxy coating

BD7053 high temperature anti abrasion wear impact corrosion chemical resistant epoxy compound ceramic coatings used in desulfurization system equipment slurry circulation pipeline rubber lining repairing and protecting

Slurry circulation pipeline,slurry circulation pipeline mainly uses butyl rubber lining rubber pipeline,it often appears rubber lining bulge,peeling,
falling off etc.phenomenon during operation.If it appears in a large area,we should peel off the rubber lining,make the combined protective coatings on the pipeline,chooses the materials of BD407,BD408 and BD7053,to form the composite coating of the outer abrasion resistant and the inner corrosion resistant.
According to the empirical data, every 2mm thickness BD7053 desulfuration absorption tower slurry pipeline rubber lining repair anti abrasion wear
corrosion chemical resistant coatings can provide 1 year effective protection for the slurry circulation pipeline.If only partial is bulge and peeling,
can clean up this part of adhesive residue,smear the BD436 rubber lining epoxy wearing compound repair agent for repairing.The BD436 rubber lining
repair adhesive wearing compound epoxy coating both has wear resistant and corrosion resistant performance,at the same time,it has higher bonding
strength to metal and rubber,according to the empirical data,every 5mm thickness can provide one year effective protection for the slurry rubber lining
pipeline during repairing.

Range of application for BD7053 absorption tower slurry pipeline ceramic rubber lining repair abrasion corrosion chemical resistant coatings:
Special used in the preparation of high temperature anti corrosion chemical abrasion wear resistant coatings to repair and protect desulfurization
absorption tower and slurry circulation pipeline.

Product packaging actual picture of BD7053 slurry circulation pipeline absorption tower protective anti corrosion
chemical abrasion resistant coating:

Construction case photo shows:


Leave a Reply

Fill in your details below or click an icon to log in: Logo

You are commenting using your account. Log Out /  Change )

Google+ photo

You are commenting using your Google+ account. Log Out /  Change )

Twitter picture

You are commenting using your Twitter account. Log Out /  Change )

Facebook photo

You are commenting using your Facebook account. Log Out /  Change )


Connecting to %s