abrasion wear resistant rubber repair agent epoxy compound ceramic coating

The advantage of BD916 anti abrasion wear resistant rubber repair agent epoxy compound:

High quality and high efficient–with excellent performance quality,double components,fast curing speed, high efficient construction impact resistant,
abrasion wearing resistant.It can replace the traditional heat vulcanization repairing and repair method of the adhesive bonding adhesive tape,the strength
surpasses the heat vulcanization.

Reliable and durable–the thickness of repairing coating is controllable,taking shape is fast,the usable time is short.The coating after curing has very high
cohesion strength,tensile strength,peel strength and good hardness,toughness and rate elongation.

Quick and convenient–Can greatly simplify the construction technology for repairing,the performance of self-leveling is good,the appearance is bright.
Can not only repair the damaged rubber conveyor belt,rubber products quickly,but also can precoat a layer of protective coating on the surface of undamaged
conveyor belt,rubber covered roller and rubber products etc,prolong the service life.Saving the adhesive–precise mixture,saving increases with the increasing
need to use,avoid waste,cost savings.

Main usage of BD916 rubber wear abrasion resistant repair compound agent:
Used in the joint repairing of steel core,the whole core and common conveyor belt horizontal and vertical tear,and repairing of the conveyor belt surface wear,
impellers,belt edge wear,belt surface perforation and joint sealing,the repairing of polyurethane composite tube,cable,rubber roller and other rubber products.

How to use of BD916 anti abrasion wearing resistant compound rubber repair agent:
1.Surface treatment: Matting on the pending-repair area with steel brush,cleaning,decontamination,degreasing and drying it by airing(we should scrub
the pending-repair areas repeatedly with acetone,ethyl acetate etc. for degreasing and cleaning,only in this way,it can achieve the good adhesive strength)

2.Configure adhesive and repair: According to the mass ratio A:B=2:1,you should stir it uniformly quickly in a dry and clean utensil(be sure not to have
water and water vapor),then pour it into the pending-repair area for floating,curing for 4~6 hours at the normal temperature before putting it into use,
curing for 48 hours can reach to the largest strength.



Leave a Reply

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out /  Change )

Google+ photo

You are commenting using your Google+ account. Log Out /  Change )

Twitter picture

You are commenting using your Twitter account. Log Out /  Change )

Facebook photo

You are commenting using your Facebook account. Log Out /  Change )


Connecting to %s