high temperature pipe sealing repair epoxy putty ceramic compound coating

BD757 high temperature wearing resistant pipeline sealing repair epoxy ceramic bead putty compound repairing,sealing and bonding of oil,water,steam,acid,alkali pipeline flange surface under various high temperature working condition.

http://www.wearcoating.com/case-of-desulfuration-pipeline-repairing-coatings/high_temperature_pipe_sealing_repair_epoxy_ceramic_putty_4638.html

Product description of BD757 wearing high temperature resistant metal pipeline sealing repair epoxy ceramic compound putty:
It’s the high temperature repairing agent consist of modified high temperature resin and high temperature curing agent,
it’s made of filling polymerization from ceramic,metal,fiber and so on,super-heated steam resistant,various acid & alkali
corrosion resistant,oil resistant,good toughness,with a high bonding strength.The touching temperature can reach to 300 degree,
can work under 250 degree for a long time.Suitable for the repairing,sealing and bonding of oil,water,steam,acid,alkali pipeline flange
surface under various high temperature working condition.

How to use of our BD757 high temperature metal pipeline repair sealing ceramic putty epoxy compound:
1.Surface treatment: Do the coarsening treatment on the pending-repair or needing-bonding area,
then clean it by cleaning agent.

2.Configuration: According to the mass ratio A:B=5:1 or volume ratio A:B=4:1, make A and B two components mix uniformly,
and use it up within specified operation time limit.

3.Coating::Make the mixed-up material spread coating on the pending-repair area layer by layer,the first layer should be compacted,
make it infiltrate fully with the substrates.

4.Curing:Cure for 24 hours at the normal temperature,or cure for 2 hours at the temperature of 25 degree,
then heat it up to the temperature of 80 degree and keep this temperature for 2 hours,if the temperature is low in winter,
can heat it up or prolong the curing time to complete the curing.

Product performance index:

product name physical state standard packaging Volume
(cm3)
operational time limit
(25℃)
curing time
(25℃)
757 high temperature sealing
agent epoxy compound repair putty
paste 500g/set
Two-component
360 30min 24h
color density
(g/cm3)
compressive strength
(kg/cm2)
GB1041-2008
shear strength
(kg/cm2)
GB7124-2008
bending strength
(kg/cm2)
GB1042-1999
hardness
(Shore D)
ASTM-D-2556
dielectric strength
(kv/mm)
working
temperature
(℃)
gray 1.4 867 120 150 86 16 -60~300

Product packaging photo of BD757 high temperature pipeline sealing agent epoxy ceramic compound repair putty:

Advertisements

Leave a Reply

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out / Change )

Twitter picture

You are commenting using your Twitter account. Log Out / Change )

Facebook photo

You are commenting using your Facebook account. Log Out / Change )

Google+ photo

You are commenting using your Google+ account. Log Out / Change )

Connecting to %s