high temperature anti abrasion wearing epoxy compound inorganic adhesive

1200N high temperature anti abrasion wearing resistant compound epoxy inorganic adhesive

http://www.wearcoating.com/high%20temperature%20resistant%20adhesive/high_temperature_wearing_epoxy_compound_inorganic_adhesive_4603.html

Performance features of BD1200N anti wear high temperature resistant epoxy compound inorganic adhesives:
1.Two components, inorganic bonding material.
2.The highest temperature resistant can reach to 1200 degree.

3.Has very high compressive shear strength
4.The amount of shrinkage for material curing process is small

5.Do not flaw
6.With strong bonding force to metal substrates.

Product usage:
Used for repairing and bonding of the workpiece under the high temperature working condition of 1200 degree,it has high bonding strength
especially for the metal substrates.

Ratio:
You could adjust the mixing mass ratio based on actual required viscosity of your working condition between mixing mass ratio A:B=2:3
to A:B=3:2.

Curing condition:
Curing for 2 hours at room temperature,and heat it up to the temperature of 60-80 degree and keep this temperature for 2 hours,then heat it up
to the temperature of 150 degree and keep this temperature for 2 hours,after that cool it down to the room temperature slowly.

Advertisements

Leave a Reply

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out / Change )

Twitter picture

You are commenting using your Twitter account. Log Out / Change )

Facebook photo

You are commenting using your Facebook account. Log Out / Change )

Google+ photo

You are commenting using your Google+ account. Log Out / Change )

Connecting to %s