metal copper anti wear abrasion resistant repair compound epoxy coating

BD114 high bonding strength two components paste epoxy coating wearing compound
used in repairing and rebuilding the brass, bronze casting and casting defects.

http://www.wearcoating.com/case-of-desulfuration-pipeline-repairing-coatings/metal_copper_repair_epoxy_coating_wearing_compound_4493.html

Product description:
It’s the high performance polymerization metal materials compounded by various alloy material and modified toughening heat resistant resin,

Product usage of BD114 copper metal epoxy repair double components coating wearing compound:
suitable for the repairing and rebirth of the brass,bronze casting and process castings defects.The color after repairing is basically the same as
the substrates,with the very high strength and excellent wear&corrosion resistance and aging resistant properties,can do various mechanical
processing together with substrates.

how to use:
Surface treatment: Do the coarsening treatment on the pending-repair surface and clean it by cleaning agent.

2.Configuration: According to the mass ratio A:B=6:1 or volume ratio A:B=4:1,make A and B two components mix uniformly,then use it up within
specified operation time limit.

3.Coating: Make the mixed-up material spread coating on the pending-repair areas layer by layer,the first layer should be compacted,make it infiltrate
fully with the substrates.If the following working procedure needs machining,should keep out appropriate machining allowance

4.Curing: Cure for 8 hours at the temperature of 25-30 degree before doing machining, cure for 24 hours before putting it into use,if the temperature is low,
should heat it up or prolong the curing time to promote the curing.

Application case photos of BD114 metal copper anti wear abrasion resistant repair compound epoxy coating:



Advertisements

Leave a Reply

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out / Change )

Twitter picture

You are commenting using your Twitter account. Log Out / Change )

Facebook photo

You are commenting using your Facebook account. Log Out / Change )

Google+ photo

You are commenting using your Google+ account. Log Out / Change )

Connecting to %s