crusher wear impact resistant protective epoxy backing compound

BD65 backing filling wearing repair epoxy compounds used in cone crusher ceramic rubber lining plate backing wear abrasion corrosion repairing and protecting
1.The surface treatment:
Clean up the crusher cone surface and lining plate inner surface,remove the surface attachments.
2.Install the liner plate:
For dynamic cone,can make the handling-well lining plate (including upper and lower segment liner plate) install on the cone directly,
seal up the seams with a silly putty, clay or cement.For cone, install the bottom two layers of lining plate first.
3. Configure adhesives/epoxy backing compound:
Make the backing material B component(small drum) pour into the backing material A component(big drum),then stir it uniformly.Had better
pre-stir the backing material A component for a few minutes before mixing,then add the curing agent B component to mix it uniformly.
When the temperature is low in winter,the viscosity of backing material A component is large,can preheat the backing material A component
up to the temperature of 25-45 degree separately,then do the stirring and mixing.
4.Using the adhesives/backing wearing compounds:
For the moving cone,make the mixed-up adhesives pour into the aperture of cone and lining plate directly,until to tank it up.For fixed cone,
make the mixed-up adhesives pour into the crack of the cone and liner plate,tank up the bottom two layers of lining plate.Then install the
middle part and top part four layers of liner plate,seal it well,make the mixed-up adhesives pour into the aperture of cone and lining plate,
until to tank it up.
5.Curing:
Place it to cure for 12 to 24 hours at room temperature(20 degree),the temperature has great effects on the curing time,the curing is fast
for high temperature,the curing is slow for low temperature,generally curing for 12 hours can be put into using in summer,curing for 24
hours in winter can be put into using,should heat for curing at low temperature.BD65 is difficult to cure,when the environment temperature
is lower than 5 degree,BD66 is difficult to cure,when the environment temperature is lower than the below zero 5 degree,if the temperature
is lower than the specified requirements during using,all need to  do the heat curing,in order to guarantee the performance of the product.
Product usage of our BD65 crusher impact abrasion repair backing filling epoxy compound:
BD65 cone crusher wearing plate filling epoxy adhesive backing compound(crusher abrasion lining plate repair epoxy filling material) is used
in the filling/supporting between crusher lining plate and substrates,gravel barrels and jacket gap,support cone and protective layer space,
at the same time it can be used as buffer material,when the equipment suffers impacting or load vibration from broken ore,
also used in the structural reinforcement,impact resistant vibration of ball mill wear resistant lining plate and cylinder gap.
Product packaging actual photo of BD65 crusher wear impact resistant protective epoxy backing compound:
Advertisements

Leave a Reply

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out / Change )

Twitter picture

You are commenting using your Twitter account. Log Out / Change )

Facebook photo

You are commenting using your Facebook account. Log Out / Change )

Google+ photo

You are commenting using your Google+ account. Log Out / Change )

Connecting to %s