high temperature anti wear abrasion resistant repair special prime coat

Product description of BD4262 high temperature abrasion wear resistant use primer coating:

http://www.wearcoating.com/abrasion%20wear%20resistant%20coating/high_temperature_wear_abrasion_resistant_prime_coating_4706.html
BD4262 is the high performance polymeric material which compounded by high temperature modified toughening heat resistant resin and
modified high temperature curing agent,it is used as the special high temperature prime coat of BD series anti wear abrasion resistant coating.

Performance index:

Product name Physical states Volume
(cm3)
Operational time limit
(25℃)
Put into using time
(25℃)
BD4262 special high temperature wear resistant prime coat fluid 350 30 min 4 hours

 

Density
(g/cm3)
Compressive strength
(kg/cm2)
GB1041-2008
Tensile strength
(kg/cm2)
GB6329-1999
Shear strength
(kg/cm2)
GB7124-2009
Bending strength
(kg/cm2)
GB1042-2008
Hardness after curing
(Shore D)
ASTM-D-2556
Suggested using temperature
(℃)
1.49 903 352 198 547 91 -60-200

How to use:
1.Surface treatment:Clean up the surface dust and greasy dirt etc of pending-repair parts,grind with anger grinder or sand blasting treatment,
clean it with cleaning agent and dry it by airing.

2.The preparation of prime coat:Make A and B two components mix uniformly according to the weight ratio A:B=3:1,and use it up within
the specified operation time limit.

3.Coating:Make the well mixed material be coating on the surface of pending-repair parts uniformly,the suitable coating thickness is about
0.2-0.5mm,make it infiltrate fully with the substrates.

Transportation storage:
Sealed storage in the cool and dry place.The warranty period is 12 months.Avoid placing it upside down, knocking against and transporting
it as a non-dangerous product during transportation.

Product packaging photo of BD4262 anti wear abrasion high temperature resistant special prime coat:

Advertisements

Leave a Reply

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out / Change )

Twitter picture

You are commenting using your Twitter account. Log Out / Change )

Facebook photo

You are commenting using your Facebook account. Log Out / Change )

Google+ photo

You are commenting using your Google+ account. Log Out / Change )

Connecting to %s