ceramic particle adhesive anti wear resistant epoxy coating

BD706 large ceramic bead filling particle adhesive epoxy compound anti abrasion wear resistant coatings used in pipeline rubber lining repairing and protecting

http://www.wearcoating.com/case-of-desulfuration-pipeline-repairing-coatings/ceramic_particle_adhesive_anti_wear_resistant_epoxy_coating_4588.html

large ceramic bead filling particle adhesive epoxy coating can fill in the ceramic tile gap of wear abrasion resistant pipeline.ceramic beads big particles
adhesive epoxy coatings is a kind of shapable anti wear abrasion resistant material,can be applied to various irregular shape,It can be largely applied during
producing wear abrasion resistant pipeline,when we use the ceramic tile to stick the anti wear abrasion resistant pipeline,it will produce gaps between
ceramic tile and another ceramic tile,this gap will affect the bonding strength of ceramic tile,when the materials scour the gaps,it will scour down the
ceramic tile,so it is the necessary step of using abrasion resistant large ceramic bead particle adhesives to fill in the gaps.

BD706 abrasion wear resistant large ceramic bead particle adhesive epoxy coating which produced by Xiangyang City Hundred Shield Coating Material
Co.,Ltd has already applied in ceramic pipeline enterprises in batch,reaction effect is very good.Large ceramic bead filling particle adhesive is compounded
by high bonding strength adhesive matching with high hardness ceramic bead particle according to the specified ratio.Our company’s anti wear abrasion
resistant epoxy coating ceramic bead big particle adhesive can compare favourably with first well-known international brands.We could offer free sample
for your testing based on customers’ working condition applications.

The construction scheme of our BD706 abrasion wear resistant coating large ceramic filling particle adhesive:
1.Surface treatment: Do the coarsening treatment on the pending-repair part,grinding with angle grinder or sand blasting etc,the surface after coarsening
treatment should be cleaned,the surface after this treatment should be the one coarsening,dry and fresh substrates,should be no greasy dirt and dust.

2.Preparation:According to weight ratio or volume ratio A:B=4:1,make A and B two components mix uniformly,and use it up within 30 min.
Generally it’s while construction and configuration.Every time the most quantity of preparation is not more than 1.5Kg,too much adhesive is solidified
too fast,hasn’t been used up until partial adhesive has solidified and can’t be used.According to the actual temperature,preparation can be appropriately
a little more in winter,proper less in summer.If the temperature is too low,can properly heat up the A component to reduce the viscosity for easy to configure.

3.Coating:The suitable coating thickness of BD706 large particle particle wear abrasion resistant coating is 2-8mm,the most thickness can be 30mm.
Make the well mixed material be coating on the pending-repair area layer by layer,the first layer should be compacted,make it infiltrate fully with the
substrates.Repair the surface to be smooth after the coating smearing in the suitable size,or use the low viscosity anti wear abrasion resistant adhesive to
smear on the surface of the coating,this material can’t do machining,so you should pay attention to controlling the coating thickness to avoid appearing
interference phenomenon in the assembly.

4.Curing:It can be put into using after curing for 24 hours at the temperature of 25 degree,if the temperature is low,should heat it up or prolong curing time
to promote the curing.General construction in winter,can use iodine tungsten lamp to do irradiation heating with 40cm distance from the coating.

Product packaging actual picture of BD706 big particle ceramic bead filling anti wear abrasion resistant coating:

Advertisements

Leave a Reply

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out / Change )

Twitter picture

You are commenting using your Twitter account. Log Out / Change )

Facebook photo

You are commenting using your Facebook account. Log Out / Change )

Google+ photo

You are commenting using your Google+ account. Log Out / Change )

Connecting to %s