metal copper epoxy repair putty wearing resistant compound

BD114 high temperature anti chemical abrasion wearing resistant metal copper epoxy repair putty compound used in repairing and protecting of the brass,bronze casting and process castings defects.
Product description of BD114 high temperature wear abrasion resistant copper metal repair compound epoxy putty:
It’s the high performance polymerization metal materials compounded by various alloy material and modified
toughening heat resistant resin,suitable for the repairing and rebirth of the brass, bronze casting and process
castings defects.The color after repairing is basically the same as the substrates,with the very high strength
and excellent wear&corrosion resistance and aging resistant properties,can do various mechanical processing
together with substrates.

how to use of BD114 metal copper high temperature wearing resistant compound epoxy repair putty:
Surface treatment: Do the coarsening treatment on the pending-repair surface and clean it by cleaning agent.

2.Configuration: According to the mass ratio A:B=6:1 or volume ratio A:B=4:1, make A and B two components
mix uniformly,then use it up within specified operation time limit.

3.Coating: Make the mixed-up material spread coating on the pending-repair areas layer by layer,the first layer should be compacted,make it infiltrate fully with the substrates.
If the following working procedure needs machining,should keep out appropriate machining allowance

4.Curing: Curing for 8 hours at the temperature of 25-30 degree before doing machining,it can be put into using after curing for 24 hours ,if the temperature is low,should heat it up or prolong the curing time to promote the curing.

Performance index:

product name physical state standard packaging volume
(cm3)
operational time limit
(25℃)
usable time
(25℃)
BD114 metal copper
rebuilding repair compound
epoxy coating
paste 250g/set
Two-component
163 45min 24h
color density
(g/cm3)
compressive strength
(kg/cm2)
GB1041-2008
tensile strength
(kg/cm2)
GB6329-2008
shear strength
(kg/cm2)
GB7124-2008
bending strength
(kg/cm2)
GB1042-1999
hardness
(Shore D)
ASTM-D-2556
working
temperature
(℃)
brass 152 922 367 273 512 87 -60~166

Product packaging actual picture of BD114 wearing high temperature metal copper repair putty epoxy compound coating:

Advertisements

Leave a Reply

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out / Change )

Twitter picture

You are commenting using your Twitter account. Log Out / Change )

Facebook photo

You are commenting using your Facebook account. Log Out / Change )

Google+ photo

You are commenting using your Google+ account. Log Out / Change )

Connecting to %s