liquid iron epoxy repair putty wearing resistant compound

BD102 liquid iron metal epoxy repair putty anti abrasion wearing resistant compound used in repairing and protecting the casting defect part of various industrial equipment

http://www.wearcoating.com/case-of-desulfuration-pipeline-repairing-coatings/liquid_iron_epoxy_repair_putty_wearing_resistant_compound_4618.html

Product description of BD102 liquid iron abrasion wearing resistant epoxy repair putty compound:
It’s the high performance polymerization metal materials compounded by various alloy material and modified toughening heat resistant resin,
used in repairing various casting defects,with the higher strength,can do various mechanical processing together with substrates.The material
after curing has the higher strength, can do various mechanical processing.With the higher bonding strength to metal,has high performance of
abrasion resistant,corrosion resistant and aging resistant.

How to use of BD102 wear abrasion resistant liquid iron metal epoxy compound repair putty:
1.Surface treatment: Do the coarsening treatment on the pending-repair surface and clean it by cleaning agent.

2.Configuration: According to the mass ratio A:B=2:1 or volume ratio A:B=2:1,make A and B two components mix uniformly,
then use it up within specified operation time limit.

3.Coating: Make the mixed-up material spread coating on the pending-repair areas layer by layer,the first layer should be compacted,
make it infiltrate fully with the substrates.If the following working procedure needs machining,should keep out appropriate machining allowance.

4.Curing: It can be doing machining after curing for 8 hours at the temperature of 25-30 degree ,it can be put into using after curing for 18 hours, if the temperature is low,should heat it up or prolong the curing time to promote the curing.

Performance index:

product name physical state standard packaging volume
(cm3)
operational time limit
(25℃)
usable time
(25℃)
BD102 liquid iron
anti wear epoxy
coating repair agent
semi-fluid 250g/set
Two-component
183 25min 18h
color density
(g/cm3)
compressive
strength
(kg/cm2)
GB1041-2008
tensile
strength
(kg/cm2)
GB6329-2008
shear strength
(kg/cm2)
GB7124-2008
bending strength
(kg/cm2)
GB1042-1999
hardness
(Shore D)
ASTM-D-2556
working
temperature
(℃)
gray 1.64 806 311 183 473 82 -60~120

Product packaging picture of BD102 liquid metal iron epoxy repair compound putty:

bd101%e5%89%af%e6%9c%ac

Advertisements

Leave a Reply

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out / Change )

Twitter picture

You are commenting using your Twitter account. Log Out / Change )

Facebook photo

You are commenting using your Facebook account. Log Out / Change )

Google+ photo

You are commenting using your Google+ account. Log Out / Change )

Connecting to %s