high temperature resistant iron repair putty epoxy compound

BD116 high temperature abrasion wearing resistant iron repair putty epoxy compound
used in repairing and protecting the gray iron,ductile iron,cast iron parts defect and iron parts wear under the high temperature working condition.


Product description of BD116 metal iron wear abrasion high temperature resistant epoxy repair putty compound:
It’s the high temperature high performance polymerization metal materials compounded by various alloy material
and modified toughening heat resistant resin.The highest temperature resistance is 300 degree,suitable for the
repairing of gray iron,ductile iron,cast iron parts defect and iron parts wear under the high temperature
working condition.The color after repairing is basically the same as the substrates,with the very high strength and
excellent wear&corrosion resistance and aging resistant properties,can do various mechanical processing
together with substrates.

How to use of BD116 high temperature wearing resistant iron metal epoxy compound repair putty:
1.Surface treatment: Do the coarsening treatment on the pending-repair or needing-bonding area,
then clean it by cleaning agent.

2.Configuration: According to the mass ratio A:B=4:1 or volume ratio A:B=4:1,make A and B two components mix uniformly,
then use it up within specified operation time limit.

3.Coating: Make the mixed-up material spread coating on the pending-repair areas layer by layer,the first layer should be compacted,
make it infiltrate fully with the substrates.If the following working procedure needs machining,should keep out appropriate machining allowance

4.Curing: Curing for 2 hours at the temperature of 25-30 degree,heat it up to the temperature of 80 degree and keep this temperature
for 2 hours or it can be put into using after curing for 24 hours at the temperature of 25~30 degree,if the temperature is low,
should heat it up or prolong the curing time to promote the curing.

Performance index:

product name physical state standard packaging volume
operational time limit
usable time
BD116 high temperature
metal iron repair agent
rebuilding epoxy compound
paste 250g/set
178 45min 24h
color density
compressive strength
shear strength
bending strength
(Shore D)
working temperature
iron cast 1.41 971 149 482 86 -60~250

Product packaging photo of our BD116 metal iron high temperature repair putty compound epoxy coating

Leave a Reply

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out /  Change )

Google photo

You are commenting using your Google account. Log Out /  Change )

Twitter picture

You are commenting using your Twitter account. Log Out /  Change )

Facebook photo

You are commenting using your Facebook account. Log Out /  Change )

Connecting to %s