aluminum metal epoxy repair putty anti wearing compound

BD113 aluminum metal epoxy repair putty anti abrasion wearing resistant compound coating used in repairing and protecting various aluminum casting defect and aluminum parts wear.

http://www.wearcoating.com/case-of-desulfuration-pipeline-repairing-coatings/aluminum_metal_epoxy_repair_putty_anti_wearing_compound_4615.html

Product usage for BD113 high temperature wear abrasion resistant metal aluminum repair putty epoxy compound:
It is suitable for the repairing of various aluminum casting defect and aluminum parts wear.The color after repairing is basically the same as the
substrates,with the very high strength and excellent wearing abrasion & corrosion resistance and aging resistant properties,can do various
mechanical processing together with substrates.

how to use of BD113 metal aluminum abrasion wearing resistant epoxy compound repair putty:
1.Surface treatment: Do the coarsening treatment on the pending-repair surface and clean it by cleaning agent.

2.Configuration: According to the mass ratio A:B=6:1 or volume ratio A:B=4:1, make A and B two components mix uniformly,then use it up within
specified operation time limit.

3.Coating: Make the mixed-up material spread coating on the pending-repair areas layer by layer,the first layer should be compacted,make it infiltrate
fully with the substrates.If the following working procedure needs machining,should keep out appropriate machining allowance

4.Curing: Curing for 8 hours at the temperature of 25-30 degree before doing machining,it can be put into using after curing for 24 hours,
if the temperature is below 15 degree,it can’t be curing fully,should heat it up to promote the curing(such as:bake it for 2 hours with the
iodine tungsten lamp)

performance index:

product name physical state standard packaging volume
(cm3)
operational time limit
(25℃)
usable time
(25℃)
BD113 metal aluminum
epoxy putty
repair compound
paste 250g/set
Two-component
177 45min 24h
color density
(g/cm3)
compressive strength
(kg/cm2)
GB1041-2008
tensile strength
(kg/cm2)
GB6329-2008
shear strength
(kg/cm2)
GB7124-2008
bending strength
(kg/cm2)
GB1042-1999
hardness
(Shore D)
ASTM-D-2556
working
temperature
(℃)
aluminum 1.40 995 334 236 514 86 -60~166

Product packaging actual picture of our BD113 aluminum metal wear abrasion resistant epoxy repair putty compound:

Advertisements

Leave a Reply

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out / Change )

Twitter picture

You are commenting using your Twitter account. Log Out / Change )

Facebook photo

You are commenting using your Facebook account. Log Out / Change )

Google+ photo

You are commenting using your Google+ account. Log Out / Change )

Connecting to %s