wear abrasion impact resistant ceramic tile adhesive

BD100 wear abrasion impact resistant ceramic tile bonding epoxy compound adhesive

http://www.wearcoating.com/abrasion%20resistant%20ceramic%20adhesive/BD100_wear_abrasion_impact_resistant_ceramic_tile_adhesive_4327.html

Performance features of our BD100 impact wear resistant epoxy ceramic tile adhesives:
1.It is the two-component adhesive compounded by polyurethane modified epoxy resin,modified amine curing agent
and various addition agent.
2.The curing speed is moderate,curing materials can resist the temperature of 100 degree
3.with a good adhesion to metal,ceramic and so on.The adhesive layers after curing have an excellent impact resistance
4. Excellent in water resistance,oil resistance and aging resistance

Product usage:
It’s used for self-adhesion and each-adhesion of metal,ceramic,cement,stone,glass and other materials,especially suitable for the adhesive of strong impact
vibration artifacts.When using in the paste of wear resistant ceramic – metal,can partial replace ceramic-rubber composite lining board.Used in the paste of various wear resistant ceramic parts,can effectively avoid knocking
against and impacting to cause the ceramic fall off during transportation or installation.

Performance index:

product name Physics
Status
standard
packaging
operation
time limit
(25℃)
curing time
(25℃)
range of application
BD100 impact abrasion
resistant ceramic adhesive
paste 12kg 1 hour 24 hours Used in the self-adhesion and each-adhesion
among metal,ceramic and wood.
Such as used in the adhesive of machine
tool bed,various box body,large module
gear fracture.Especially suitable for
the adhesive of strong shock vibration artifacts
item color density
(g/cm3)
shear strength
(kg/cm2)
GB7124-2008
impact strength
(J/cm2)
GB6328-1999
tensile strength
(kg/cm2)
GB6329-2008
peel strength
(N/cm)
Working temperature
(℃)
BD100 black 1.11 256 180 685 12 -60~100

How to use:
1.Surface treatment: Grinding or sand blasting to clean up the dust,oil and rust of sticking surfaces,
finally wash it with cleaning agent and dry it by airing.

2.Adhesive preparation:According to the ratio of A:B=2:1,make the A and B two components uniform mixing,
when the temperature is very low,can respectively put the main agent and curing agent into 50℃ environment to preheat and
mix up,then according to a given proportion of weighing,mix and stir uniformly.

3.Sizing:put the mixed-up adhesive spread to coat onto the surface of pending-sticky material,then fold it,from the middle to all around,knock it on with a rubber hammer for a time,avoid the air getting into it.

4.Curing:Curing:initial curing will take 4 hours at the room temperature,fully curing will take 24 hours (18~22Mpa),
if heat it up to the temperature of 80 degree,keep this temperature for 2 hours,you can do post curing.In this way,it will get higher comprehensive performance
(can improve 30%)

Notice:
This product is general chemicals,in the process of transportation storage,you should pay attention to waterproof,fire prevention,
a cool and dry place preservation,storage period is 12 months.

Product packaging photo of BD100 anti wear abrasion imapct chemical resistant ceramic tile bonding epoxy adhesive

Advertisements

Leave a Reply

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out /  Change )

Google photo

You are commenting using your Google account. Log Out /  Change )

Twitter picture

You are commenting using your Twitter account. Log Out /  Change )

Facebook photo

You are commenting using your Facebook account. Log Out /  Change )

Connecting to %s