small particles wearing abrasion resistant repair compound epoxy coatings

BD707 small particle ceramic anti wear abrasion resistant coating,anti abrasion wearing resistant small ceramic bead particles epoxy repair compounds

Product description:
BD707 small particle ceramic beads filling repair epoxy compound anti abrasion wear resistant coating is the high performance
wear/abrasion & corrosion resistant polymerization ceramic material compounded by high performance wear resistant ceramic
particle and modified toughening heat resistant resin.Widely used in the repairing of various wear-out part and the preparation of
abrasion wear resistant,corrosion resistant coating on the surface of various machine part which has wear resistant,corrosion
resistant requirements.

Product features of our BD707 anti wear abrasion resistant repair epoxy small particle coating:
1.With very high bonding strength to metal substrates
2.Don’t flow,good form-ability,with fast curing speed and good operation manufacture-ability
3.Suitable for the repairing and protecting of various wear abrasion,corrosion working condition.

Performance index of our BD707 small particles wearing abrasion resistant repair compound epoxy coatings:

product name physical state operation time limit
Usable time
range of application
BD707 small particle wear abrasion resistant repair compound epoxy coating paste 30 min 24 hours Two component,widely used in the repairing of various wear-out part and the preparation of wear resistant protective coating on the surface of various machine part which has wear & corrosion resistant requirements.such as:the repairing and pre-protecting of pipe, elbow, slurry pump, pumping sand pump, centrifuge, packing boxes, power plant desulfurization system slurry circulating pump body, impeller,concentric reducer etc.
color density
compressive strength)
tensile strength
shear strength
bending strength
hardness after curing
(Shore D)
the highest temp. Resistance/recommended using temp.)
dark gray 2.4 1006 377 120 516 88 160/-60-110

How to use
1.Surface treatment:

Do coarsening treatment on the pending-repair part,grinding with angle grinder or sand blasting etc,the surface after coarsening
treatment should be cleaned,the surface after this treatment should be the one coarsening,dry and fresh substrates,
should be no greasy dirt and dust.

According to weight ratio or volume ratio 4:1, make A and B two component mix uniformly,and use it up within 30 min.
Generally it’s while construction and configuration.Every time the most configuration quantity is not more than 4Kg,
too much adhesive is solidified too fast,hasn’t been used up until partial adhesive has solidified and can’t be used.
According to the actual temperature,configuration can be properly a little more in winter,proper less in summer.If the
temperature is too low,can properly heat up the A component to reduce viscosity for easy to configure.

The suitable coating thickness of BD707 small particle anti wear abrasion repair coating epoxy compound is 2-8mm,the most
thickness can be 30mm.Make the mixed-up material be coating on the pending-repair part layer by layer,the first layer should
be compacted,make it infiltrate fully with the substrates.Repair the surface to be smooth after the coating is coated in the
suitable size.If the surface has high requirements,can make BD426 corrosion resistant repair agent be coating on the surface
as the topcoat, this material can’t do machining,should pay attention to controlling the coating thickness to avoid appearing
interference phenomenon in the assembly.

It can be put into using after curing for 24 hours at the temperature of 25 degree,(If you can heat it up to the temperature of
60-80 degree and keep this temperature for 2 hours, in this way,can improve 30% comprehensive performance) If the
temperature is below 10℃,should heat it up or prolong curing time to promote the curing.General construction in winter,
can use iodine tungsten lamp do irradiation heating with 40cm distance from the coating.

Packaging specification
Two components,10Kg/group; packed in a plastic drum. A component: 8Kg/drum, B component: 2Kg/drum

Transportation storage
1.Sealed storage in the cool and dry place.The warranty period is 12 months
2.Avoid placing it upside down, knocking against and transporting it as a non-dangerous product during transportation.

Special version:
1.This parameter is for laboratory conditions,due to the actual working condition is more complex,suggest the users to do the
pretest according to actual working condition

2.When the environment temperature is below 15℃,the curing time will prolong,should take proper heating measure

3.When the environment temperature is more than 25℃ or the mixing quantity is too large,the curing speed will expedite,
should properly shorten the application time of coating after mixing.

Construction protective measures:
1.Wear the protective masks,wear the protective glasses and rubber gloves
2.Need washing hands with soap before eating,drinking or smoking.
3.The health hazard after touching: a few people will have skin allergy phenomenon,see a doctor in time and avoid touching
with this product again.should wipe it with ethyl acetate when the sizing material paste on the skin by careless,then wash it with
clear water.Should wash it with clear water immediately and see a doctor when splashing into the eyes by careless.

Warm Prompt:
Residual adhesive solution cured products are non-toxic harmless organic solid,but maybe it will produce poisonous gas
when burning,non-professional personnel can not do combustion disposal,should be sent to garbage power plant or garbage
burning place treatment.

Fire prevention measures:
Should choose dry powder to extinguish fire,can cover and flap it with dry powder,grit(the construction using abrasive) or
the non chemical fiber fabric when the sizing material catching fire.

 Product packaging actual photo of BD707 anti abrasion wearing resistant small particle epoxy repair compound:

Leave a Reply

Fill in your details below or click an icon to log in: Logo

You are commenting using your account. Log Out /  Change )

Google photo

You are commenting using your Google account. Log Out /  Change )

Twitter picture

You are commenting using your Twitter account. Log Out /  Change )

Facebook photo

You are commenting using your Facebook account. Log Out /  Change )

Connecting to %s